My Cart

Close

Teckwrap

Matte Metallic Vinyl Wrap - MT Series (MT01-05)

$ 99.99

MT05

Specifications

Conformable and reliable Renolit polymeric material. Suitable for full car wrapping (or any other smooth or curved surface).

The thickness of film: 0.12mm
The thickness of film with release liner: 0.28mm

Type of film: Pressure sensitive high-grade polymeric vinyl film with air release channels 
Colors: HM01 Dark grey silk, HM02 Brown grey silk, HM03 Sage silk, HM06 Aubergine silk, HM07 Green black silk

Series: 190 series
Glue:  Henkel solvent-based adhesive
Release liner: White silicone-coated paper with a double-sided polyethylene coating
Storing period: 3 years if stored in +10°С to +20°С for optimal quality, relative humidity 50%, in original package, away from direct sunlight, clean and dry place
Indoor life: 5 years when followed rules of application and use
Outdoor life: 3 years when followed rules of application and use
Post heating: 100 Celcius
Surface gloss (CD): 14.5% (Test method: ASTM D523-99 60 d.angle)

Elongation/Break MD:206.8 / CD:196.4 (Test method: ASTM D882-02)

Tensile Strength: MD:29.5 / CD:24.8 N/mm2 - Speed 200mm/min (Test method: ASTM D882-02)

Dimensional Stability: 2% - Oven/10'*70C(MD) (Test method: ASTM D1204-02)

Surface Tension: 34 dynes/cm (Test method: ASTM D2578-04a, 24 hours after production)

Package:  Roll width 152 cm, length 18 m, weight 13 kg

Install tips:

Temperature: from +17°С to +25°С, usage from -55°С to +65°С
Tools: Standard squeegee with soft (wet) buffer
Conformability: smooth and medium curved surface
Directional: yes
Overlap width: 3-4mm

Important note: The images, colors, and finishes on screen are approximate. For the real representation of the product always check the color swatch. Rolls from the same production LOT number should be used for completing a wrap job as a slight batch to batch variation of color may occur. The film may scratch during the application, or during a day in and out use. The scratching of the film is not covered by the warranty.